SPECIFICATIONS
| 1 | Abrasion Resistance (WeigHt Loss) | ASTM D 4060 | 1064mg |
| 2 | Lzod Impact Strength | ASTM D 256(Method A) | 13.3J/m |
| 3 | Boiling Water Resistance | NEMA LD3 2000 3.5 | No Effect |
| 4 | Colorfastness | ANZI Z124.6.5.1 | Pass |
| 5
|
Compression Strength(Dry)
Compression Strength(Wet) |
ASTM C 170
ASTM C 170 |
209 MPa
203 MPa |
| 6 | Density | KSF 2530 | 2.3-2.4 g/cm3 |
| 7
|
Deflection Temperature
Under Load (1.82 MPa) |
ASTM D 648 |
243°C |
| 8 | Flammability
Flame Spread Smoke Developed |
ASTM-84,NFPA 255 |
Class A Class A |
| 9
|
Flexural Modulus
Flexural Strength |
ASTM D 790
ASTM D 790 |
39.7 GPa
42.4 MPa |
| 10 | Freeze & Thaw Cycling | ASTM C 1026 | Unaffected |
| 11 | Fungal & Bacterial Resistance | ASTM G 21 | No Growth |
| 12 | Barcol Hardness | ASTM D 2583 | 86 |
| 13 | Rockwell Hardness(HRM) | ASTM D 785(Procedure A) | 115 |
| 14 | Point Impact | ANSI Z124.6.4.2.1 | Pass |
| 15 | Slip Resistance:
Static Cofficient of Friction(Dry) Static Cofficient of Friction(Wet) |
ASTM C1028 ASTM C1028 |
0.67 0.49 |
| 16 | Stain Resistance | ANSI Z124.6.5.2 | Pass |
| 17 | Tensile Strength | ASTM D 638 | 17.8 MPa |
| 18 | Thermal Expansion | ASTM D-696 | 1.52 10-5 in/in/°C |
| 19 | Water Absorption:
Long-term & Short-term |
ASTM D 570(24hr. Immersion) |
<0.011% |
| 20 | Wear and Cleanbility | ANSI Z124.6.5.3 | Pass |
QUARTZ SURFACE GUIDE - SPECIFICATIONS
| QJstone | Thickness Inch(cm) | Width Inch(mm) | Length Inch(mm) |
| Standard | 1 1/8 “(3cm)
3/4″(2cm) 1/2″(1.2cm) |
63″(1600mm)
63″(1600mm) 63″(1600mm) |
126″(3200mm)
126″(3200mm) 126″(3200mm) |
| Customized | 1 1/8″(3cm)
3/4″(2cm) |
Cutting to designated size
|
|